Product Details

Alkyl Phenolic Resin (SP: 115-130℃)

Item no.: APU-20-52G

Key features：
- Softening point (Ring & Ball): 115-130℃
- Enhance the adhesion strength
- Increase the phasing stability
- Increase the heat resistance
- Improve the tackiness retention time

Add to inquiry cart

Product Introduction

Application
Printing coating agents, adhesive tackifier, printing ink, paint, synthetic leather and PVC leather to enhance the adhesive viscosity.

Introduction
Though chloroprene rubber has an excellent weathering, oil and chemical resistance, it is necessary, in practice, to make use of a modifying agent to improve the properties of chloroprene rubber adhesive, such as tackiness retention time, phasing stability, heat resistance and adhesion strength. Alkyl phenolic resin "APU-20-52G" is excellently compatible with chloroprene rubber and an indispensable modifying agent for chloroprene rubber for manufacturing adhesive to meet specific purposes.

Alkyl phenolic resin

1) Specifications
ITEM NO.	Appearance	MgO Reactivity (%)	Softening point (℃, R&B)
APU-20-52G	Pale yellow, lump	6.5	115-130

2) Typical Formulation (MgO Prereation)
Part 1	Parts by wt.
Chloroprene TA-50	100
MgO	4
ZnO	5
Stabilizer	2
Part 2	Parts by wt.
APU-20-52G	50
Toluene	150
MgO	5
Water	0.5
Part 3	Parts by wt.
Toluene	96
n-Hexane	123
Ethyl acetate	123
(Solvent formula in total : Toluene/n-Hexane/Ethyl acetate = 2/1/1) Procedure Mix ingredients of Part 1 together on milling roll then dissolve in mixed solvent (Part 3). Stir Part 2 in a vessel for 5 hours, then add it the mixture of Part 1 and Part 3. Keep agitation further 5 hours to give adhesive of 25% solids.

3) Adhesive Properties
ITEM NO.	Adhesion Strength			Tackiness Retention	Heat Resistance	Phasing Resistance
	After 5 hours	After 24 hours	At 60℃
APU-20-52G	B	B	B	B	B	B
A: Excellent B: Good C: Fair X: Poor

a) Heat Resistance
ITEM NO.	Heat Resistance (℃)	Result
APU-20-52G	84	B

Test Conditions
Method	ASTM-D-816-55
Weight	500g
Adherend	Steel to vulcanized rubber
Test Conditions	Kept 3 days after bonding
Temperature graduation	2℃/5 min

b) Phasing Resisttance Adhesives in stoppered jar were kept for one month at 20℃ then phasing was observed
Excellent	Completely no phasing
Good	Top part is slightly phasing
Fair	5% of upper part is phasing
Poor	50% of adhesive is phasing

c) Tackiness Retention Time
ITEM NO.	Tackiness Retention Time	Result
APU-20-52G	10 min, 15 sec.	B

d) Adhesion Strength Test Conditions
Peeling angle	180^°
Adhesion strength at 60℃	Test pieces were kept 3 days after bonding then kept one hour at 60℃ before test.
Adherend	Steel to canvas
Peeling velocity	200 mm/min
Temperature	20℃ (68℉)

ITEM NO.	Elapsed Days				At 60℃		Initial Strength
ITEM NO.	1	3	7	Result	1 hour	Result	5 hour	Result
APU-20-52G	4.8	11.6	14.5	B	6.4	B	2.5	B
Unit : kg/25 mm

e) Shear strength
Shearing velocity	50 mm/min
Glued area	10 mm x 25 mm
Test Conditions	at 20℃ (68℉)
Open time	10 min
Bonded material	Plywood to plywood

ITEM NO.	Elapsed Days			Result
	1	3	7
APU-20-52G	22.2	32.8	43.0	B
Unit : kg/25 mm²

Taiwan PU Corporation is a professional alkyl phenolic resin manufacturer, alkyl phenolic resin producer. We supply high quality alkyl phenolic resin products, have an experienced technical team and offer the best price to alkyl phenolic resin.

Alkyl phenolic resin is called phenol formaldehyde resin for adhesive, phenolic resin for adhesive, phenolic resin tackifier for adhesive. If alkyl phenolic resin is needed, please contact us.

Product

Alkyl Phenolic Resin (SP: 115-130℃)

Item no.: APU-20-52G

Product Introduction

Related Products

Alkyl Phenolic Resin (SP: 118-125℃)

Terpene Phenolic Resin (SP: 145-160℃)

Terpene Phenolic Resin (SP: 125℃)